Softflex® 0954
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Softflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NwkgU7_Softflex-0954.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Softflex® 0954 is a Thermoplastic Elastomer (TPE) product. It can be processed by coating or injection molding and is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | ASTM D1238 | ||
| 200°C/5.0 kg | 21 | g/10 min | |
| 235°C/1.0 kg | 19 | g/10 min | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 3.2 | % | |
| Across Flow : 3.18 mm | 3.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 68 to 78 | ||
| Shore A, 10 sec | 64 to 74 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-22 Wheel) | 238 | mg | ASTM D3389 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (100% Strain) | 7 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 50% Strain | 2.57 | MPa | |
| 100% Strain | 3.27 | MPa | |
| 300% Strain | 4.90 | MPa | |
| Tensile Strength 2(Yield) | 9.54 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 810 | % | ASTM D412 |
| Tear Strength | 45.5 | kN/m | ASTM D624 |
| Compression Set 3 | ASTM D395B | ||
| 23°C, 22 hr | 24 | % | |
| 70°C, 22 hr | 78 | % | |
| 100°C, 22 hr | 96 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Impact (-30°C) | > 36.2 | J | ASTM D5420 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Overmold Bonding | ABS, PC, ABS/PC, PPO |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 to 60.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 160 to 182 | °C | |
| Middle Temperature | 171 to 193 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Nozzle Temperature | 199 to 216 | °C | |
| Processing (Melt) Temp | 193 to 210 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Injection Pressure | 34.5 to 41.4 | MPa | |
| Holding Pressure | 27.6 to 31.0 | MPa | |
| Back Pressure | 0.517 to 1.03 | MPa | |
| Screw Speed | 20 to 40 | rpm |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 510 mm/min |
| 3 . | 25% Deflection |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V932 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Texalan® 4 Series 490A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 4 Series |
| Bergamid™ A700 G15 H NC020 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Diakon® TD525 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Ducaseal Static | Dugdale Plc | PVC, Flexible | Ducaseal |