Starpylen HU 30BF4
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eWex1A_Starpylen-HU-30BF4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen HU30BF4 is a 30% Bamboo Fiber Reinforced Polypropylene Injection Molding Resin (also known as HU30BF4). (PRELIMINARY DATASHEET) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.7 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (4.00 mm) | 0.50 to 1.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 59.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 14 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 86.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 185 to 195 | °C | |
| Middle Temperature | 185 to 195 | °C | |
| Front Temperature | 185 to 195 | °C | |
| Processing (Melt) Temp | 185 to 195 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1371 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| VINIKA® CE55EG | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Badamid® A70 L | Bada AG | Nylon 66 | Badamid® |
| ECOTRAN® E 5060G NC AS | A. Schulman Europe | PPS | ECOTRAN® |
| Karina WHITE PVC COMPOUND 800-10/177-Y-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |