KW Plastics KW 621-T20
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | KW Plastics |
| Trademark: | KW Plastics |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GNVuib_KW-Plastics-KW-621-T20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Copolymer Impact Polypropylene with 20% Talc Post-Consumer Resin Injection Molding CHARACTERISTICS 20% talc reinforced for improved stiffness, heat distortion, shrink rate and cycle time. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648B | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed | 60.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6000/10 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| UBESTA 3030 U | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Nypol® PA A3 HS NTLA013 NR323 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Kingfa ABP-1507 | Kingfa | PP, Unspecified | Kingfa |
| LNP™ LUBRICOMP™ IFL36 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |