Radel® R-5600
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Radel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q5CUlT_Radel-R-5600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Radel® R-5600 is a very high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer exceptional hydrolytic stability and toughness superior to other commercially-available, high-temperature engineering resins. They also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties. Additonal Radel® grades include a transparent injection molding grade (R-5000), an opaque, general purpose, injection molding grade (R-5100) and a transparent, extrusion grade (R-5500).
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (365°C/5.0 kg) | 34 to 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.37 | % | |
| Equilibrium | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 2340 | MPa | ASTM D638 |
| Tensile Strength (3.18 mm) | 70.3 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 7.2 | % | |
| Break, 3.18 mm | 60 to 120 | % | |
| Flexural Modulus (3.18 mm) | 2340 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain, 3.18 mm) | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 690 | J/m | ASTM D256 |
| Tensile Impact Strength (3.18 mm) | 399 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 207 | °C | ASTM D648 |
| Glass Transition Temperature 1 | 220 | °C | DSC |
| CLTE - Flow (3.18 mm) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (3.18 mm) | 9.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 0.0254 mm | > 200 | kV/mm | |
| 3.18 mm | 15 | kV/mm | |
| Dielectric Constant (3.18 mm, 60 Hz) | 3.44 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2(0.762 mm) | V-0 | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Refractive Index | 1.672 | ASTM D542 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Steam Sterilization - w/ Morpholine 3 | > 1000 | Cycles |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 2.5 | hr | |
| Processing (Melt) Temp | 360 to 391 | °C | |
| Mold Temperature | 138 to 163 | °C | |
| Screw Compression Ratio | 2.2:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 171 | °C | |
| Drying Time | 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | Heating rate of 36°F (20°C) per minute. |
| 2 . | These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 3 . | Cycles passed without cracking, crazing, or rupture.Steam Autoclave Conditions:- Temperature: 270°F (132°C)- Time: 30 minutes/cycle- Steam Pressure: 27 psig (0.19 MPa)- Stress Level: 1000 psi (7.0 MPa) in flexure- Additive: Morpholine at 50 ppm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® F34 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Sanren M800E (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| NYCOA Polyamide 5300 HS | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| AMTOPP TE30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Wuxi Jiahong EB-2073A | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |