BESTPOM C09T/01
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BlEEds_BESTPOM-C09T-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Acetal copolymer resin natural standard of MFI 9 with lubrified and friction improved (PTFE) is perfect for final pieces that requires a minor wear out in final applications, inertia to different chemical products and good resistance to humidity. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 2.1 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.18 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2 |
| Tensile Stress | 44.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Electric Strength | 16 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® A AM3 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| Arak LLDPE HD5218EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| ENFLEX V1067A BLK UV | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| KRATON® G1654 H | Kraton Polymers LLC | SEBS | KRATON® |
| Karina BLACK PVC COMPOUND -E 48/ 23-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |