RTP 800 GB 20
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7nyM8K_RTP-800-GB-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Bead |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 - 2.6 | % | ASTM D955 |
| Moisture Content | 0.15 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength | 46.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2960 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 450 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 182 - 218 | °C | |
| Mold Temperature | 79.4 - 107 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® E 75 HV | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Flexathene® PD907 | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Latene® 7H2W T-V0 | LATI S.p.A. | PP Homopolymer | Latene® |
| INELEC PBTCF30 | Infinity LTL Engineered Compounds | PBT | INELEC |
| Polimid A 30 GF V0A | Poliblend S.p.a. | Nylon 66 | Polimid A |