LNP™ THERMOCOMP™ MB006S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zvOmPm_LNP-THERMOCOMP-MB006S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* MB006S is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MB-1006 HS Product reorder name: MB006S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.2 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 1.1 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 24.3 | MPa | ASTM D638 |
| Yield | 24.4 | MPa | ISO 527-2 |
| Break | 19.5 | MPa | ASTM D638 |
| Break | 19.4 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.3 | % | ASTM D638 |
| Yield | 5.5 | % | ISO 527-2 |
| Break | 88 | % | ASTM D638 |
| Break | 83 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2140 | MPa | ASTM D790 |
| -- | 2900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 44.0 | MPa | ASTM D790 |
| -- | 46.9 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 21 | J/m | ASTM D256 |
| 23°C 1 | 2.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 230 | J/m | ASTM D4812 |
| 23°C 2 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.70 | J | ASTM D3763 |
| -- | 1.59 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 75.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA V300 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Vistalon™ 404 | ExxonMobil Chemical | EPM | Vistalon™ |
| Borealis PP RD734CF | Borealis AG | PP Random Copolymer | Borealis PP |
| HiFill® PPS GF40 BK | Techmer Engineered Solutions | PPS | HiFill® |
| Huafon JF-W-DP4090 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |