Sarlink® TPV 24564
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zVFtKo_Sarlink-TPV-24564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPV 24564 is a thermoplastic vulcanized rubber (TPV) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Sarlink®The main characteristics of TPV 24564 are: flame retardant/rated flame. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 68 | ASTM D2240 | |
| Shaw A, 5 seconds | 64 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 5.17 | MPa | ISO 37 |
| Tensile Elongation (Break) | 350 | % | ISO 37 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 23 | % | ASTM D395 |
| 70°C, 22 hr | 36 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Xenon Weatherometer | SAE J1960 | ||
| Elongation Retention, 2000 hrs | 78 | % | SAE J1960 |
| Tensile Retention, 2000 hrs | 84 | % | SAE J1960 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 173 - 213 | °C | |
| Middle Temperature | 179 - 219 | °C | |
| Front Temperature | 184 - 224 | °C | |
| Nozzle Temperature | 190 - 230 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 35.0 - 60.0 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 204 | °C | |
| Cylinder Zone 2 Temp. | 171 - 210 | °C | |
| Cylinder Zone 3 Temp. | 177 - 216 | °C | |
| Cylinder Zone 5 Temp. | 182 - 221 | °C | |
| Die Temperature | 190 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA66 ZRPA66 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| Sindustris PC GN2302F | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Electrafil® PA6/6 05002 | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Iupiace® AH80 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LNP™ THERMOCOMP™ RF0069SZ compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |