TAISOX 3214
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zOXvEP_TAISOX-3214.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 3214 is a linear low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molded film. The main features of TAISOX 3214 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 142 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 157 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 40.2 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 31.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 620 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 840 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 220 | g | ASTM D1922 |
| TD : 38 µm, blown film | 560 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 47 | ASTM D2457 | |
| Clarity | 53.0 | ASTM D1746 | |
| Haze (38.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Blow Up Ratio: 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durethan® AKV 325 H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |
| INEOS PP 400-GA03 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |
| EnviroPCABS 3018G16 | West Michigan Compounding | PC+ABS | EnviroPCABS |
| Sylvin 4200-85UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Lustran® 308 NR | INEOS Styrolution Group GmbH | ABS | Lustran® |