Andur M-22 (97% HQEE/ 3%TMP)

Category:	PUR-Ester/MDI , Polyurethane (Polyester, MDI)
Manufacturer:	Anderson Development Company
Trademark:	Andur
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zMsVNG_Andur-M-22-97-HQEE-3-TMP-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Andur M-22 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications.

General Information
Forms	Liquid

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shaw A	94	ASTM D2240
Shaw D	45	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Compressive Strength			ASTM D695
2% strain	0.965	MPa	ASTM D695
5% strain	1.90	MPa	ASTM D695
10% strain	3.10	MPa	ASTM D695
15% strain	3.72	MPa	ASTM D695
20% strain	5.17	MPa	ASTM D695
25% strain	6.55	MPa	ASTM D695
50% strain	18.6	MPa	ASTM D695
Taber Abrasion Resistance	42.0	mg	ASTM D1044

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
100% strain	7.58	MPa	ASTM D412
300% strain	14.5	MPa	ASTM D412
Tensile Strength (Yield)	41.4	MPa	ASTM D412
Tensile Elongation (Break)	600	%	ASTM D412
Compression Set	34	%	ASTM D395

Thermoset	Nominal Value	Unit
Pot Life	6.0 - 10	min
Demold Time	90	min

Additional Information
Die C Tear, ASTM D1004: 805 pliAverage Split Tear, ASTM D1938: 320 pliStoichiometry Curative Level: 90%Break Set, ASTM D412-80: 30%NBS Abrasion: 250% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 13.7 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 13.8 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 13.91 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 14.01 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 14.12 parts by weightMix Temperature: Andur M-22: 221-230°F Curative HQEE/TMP: 230°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours

Additional Information

Die C Tear, ASTM D1004: 805 pliAverage Split Tear, ASTM D1938: 320 pliStoichiometry Curative Level: 90%Break Set, ASTM D412-80: 30%NBS Abrasion: 250% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 13.7 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 13.8 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 13.91 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 14.01 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 14.12 parts by weightMix Temperature: Andur M-22: 221-230°F Curative HQEE/TMP: 230°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours

Injection	Nominal Value	Unit
Mold Temperature	110 - 140	°C

Resin Grade	Manufacturer	Category	Trademark
Quadrant EPP Sanalite® HDPE	Quadrant Engineering Plastic Products	HDPE	Quadrant EPP
SABIC® PPcompound 2632-8	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
Vistalon™ 6602	ExxonMobil Chemical	EPDM	Vistalon™
Geon™ Vinyl Rigid Extrusion 85857	PolyOne Corporation	PVC, Rigid	Geon™ Vinyl Rigid Extrusion
NORYL™ WCV072 resin	SABIC Innovative Plastics	PPE+PS+PP	NORYL™