INEOS HDPE K44-11-128
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zKgAtx_INEOS-HDPE-K44-11-128.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| K44-11-128 is a high molecular weight, high density polyethylene copolymer for large part blow molding. It combines excellent processability and outstanding physical performance, particularly environmental stress crack resistance (ESCR) and impact properties. This resin meets the Food and Drug Administration requirements of 21CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.947 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 12 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (100% Igepal, F50) | > 2000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 24.1 | MPa | |
| Break | 37.9 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 11 | % | |
| Break | 900 | % | |
| Flexural Modulus | ASTM D790A | ||
| 2% Secant | 841 | MPa | |
| Tangent | 1130 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 310 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | 30.3 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 65.0 | °C | |
| 1.8 MPa, Unannealed | 45.0 | °C | |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP652P | PolyMirae | PP Homopolymer | Moplen |
| Altuglas® HFI-10 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Hanwha Total PE P110BL | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| KEBATER® PBT B510 | BARLOG plastics GmbH | PBT | KEBATER® |
| Sylvin 9067-90 Orange 566 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |