Primocon M90
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | Primocon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 75PbU2_PrimoconM90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Primocon M90 is an Acetal Copolymer. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.9 | % | ISO 294-4 |
| Flow | 2.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.75 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ISO 527-2/1A/1 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2450 | MPa | ISO 899-1 |
| 1000 hr | 1350 | MPa | ISO 899-1 |
| Flexural Modulus (23°C) | 2550 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1e | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1e |
| 23°C | 6.0 | kJ/m² | ISO 179/1e |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 180 | kJ/m² | ISO 179/1eU |
| 23°C | 190 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.7 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 101 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 8.0E+12 | ohms·cm | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 V33 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| AIE PET 40G3F | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| Fainplast PVC GS 69/T | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Gallonprene® GP310-6003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LNP™ THERMOTUF™ IX02582 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOTUF™ |