VICTREX® PEEK 450CA40

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	zFynXd_VICTREX-PEEK-450CA40.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, 40% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low flow, FDA food contact compliant, colour black.

Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 40% filler by weight
Features	Semicrystallization Low friction coefficient Rigidity, high High strength Low liquidity Good chemical resistance Good wear resistance Compliance of Food Exposure
Agency Ratings	FDA Food Exposure, Not Rated
Appearance	Black
Forms	Particles
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.44	g/cm³	ISO 1183
Spiral Flow	6.50	cm	Internal method
Molding Shrinkage ²			ISO 294-4
Vertical flow direction	0.50	%	ISO 294-4
Flow direction : 200°C	0.10	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.030	%	ISO 62
Balance, 23°C, 3.20mm, 50% RH	0.30	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 23°C)	88		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	35000	MPa	ISO 527-2
Tensile Stress (Break, 23°C)	270	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	1.4	%	ISO 527-2
Flexural Modulus (23°C)	30000	MPa	ISO 178
Flexural Stress (23°C)	400	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	10	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	45	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	143	°C	ISO 3146
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : < 143°C	5.0E-6	cm/cm/°C	ISO 11359-2
Flow : > 143°C	8.0E-6	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	3.5E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	9.0E-5	cm/cm/°C	ISO 11359-2
Specific Heat Capacity	1800	J/kg/°C	DSC

Flammability	Nominal Value	Unit	Test Method
Toxicity			NES 713
CO Content	0.0500		NES 713
CO2 Content	0.120		NES 713
Total Gases	0.170		NES 713

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ³(23°C)	1.0E+5	ohms·cm	ASTM D4496

Flammability	Nominal Value	Unit	Test Method
Glow Wire Flammability Index (2.00 mm)	960	°C	IEC 60695-2-12

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	850	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	380	°C
Middle Temperature	390 - 395	°C
Front Temperature	400	°C
Nozzle Temperature	405	°C
Mold Temperature	190 - 210	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	405°C nozzle
3 .	1V

Resin Grade	Manufacturer	Category	Trademark
Rigidex® P 450-HP90	INEOS Olefins & Polymers Europe	PP Impact Copolymer	Rigidex® P
SIBUR Synthetic Rubber SKN 3365 E	SIBUR, LLC	NBR	SIBUR Synthetic Rubber
Syncure™ System S100NA	PolyOne Corporation	XLPE	Syncure™
TOTAL Polystyrene Crystal 1441	TOTAL Refining & Chemicals	PS (GPPS)	TOTAL Polystyrene
NOVALAC FM 4004F	Vyncolit N.V.	Phenolic	NOVALAC