FARALLOY® PS-101
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | O'Neil Color and Compounding |
| Trademark: | FARALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iYC9k8_FARALLOY-PS-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FARALLOY PS-101 is an extrusion grade high impact polystyrene formulated to resist ignition as defined by Underwriters' Laboratories 94V test protocol. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 55 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 53.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 76.7 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.1 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | ||
| 4.24 mm | 5VA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA6G25-BK10 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| Pro PP-CO-40T | Pro Polymers | PP Copolymer | Pro-Comp™ |
| REXtac® APAO RT 2732 | Huntsman Corporation | PAO | REXtac® APAO |
| VENELENE® 7700M | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| 3M™ Dyneon™ Fluoroelastomer FC 2152 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |