Bapolene® 105F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yizEMv_Bapolene-105F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene LD105F is an unmodified low density polyethylene which extrudes into a low gloss high impact film. It contains antiblock additives and no slip additives. This product meets the Food and Drug Administration requirements of 21CFR177.1520. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 200 µm | ||
| Secant Modulus 1 | ASTM D882 | ||
| MD | 159 | MPa | |
| TD | 179 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 24.1 | MPa | |
| TD : Yield | 20.7 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 350 | % | |
| TD : Break | 600 | % | |
| Dart Drop Test | 83.0 | kN/m | ASTM D1709 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 0.10 mm/min |
| 2 . | 250 mm/min |
| 3 . | 250 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1550 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Miramid® DB2010CW | BASF Leuna GmbH | Nylon 6 | Miramid® |
| NORYL™ FXN121BK resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| ALCOM® ASA 540/6 UV SV1245-05MCF | ALBIS PLASTIC GmbH | ASA | ALCOM® ASA |
| Sylvin 9925-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |