KOPA® KN135HB40SIBL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yXBMLy_KOPAKN135HB40SIBL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA®KN135HB40SIBL is a polyamide 6 (nylon 6) product,. It can be processed by injection molding and is available in North America, Latin America, Europe or Asia Pacific. KOPA®KN135HB40SIBL application areas include engineering/industrial accessories and automobile industry. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.45 | g/cm³ | ASTM D792 |
| -- | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 142 | MPa | ASTM D638 |
| 23°C | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.0 | % | ASTM D638 |
| Fracture, 23°C | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10800 | MPa | ASTM D790 |
| 23°C | 6900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 240 | MPa | ASTM D790 |
| 23°C | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 205 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 190 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 184 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.50 | ASTM D150 | |
| Arc Resistance | 136 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80 - 100 | °C | |
| Drying Time - Desiccant Dryer | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 255 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP CX03-81 | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PP |
| Tecnoprene® AK6HI NAT001 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| Telcar® 90-E607B-75NT | Teknor Apex Company | EVA | Telcar® |
| Nipol® LX851E | Zeon Corporation | Latex | Nipol® |
| IDI SMC S20 (Glass Content 10%) | IDI Composites International | TS, Unspecified | IDI SMC |