APTIV® 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications. APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom. APTIV 1000 has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 0.0500 mm, 50% RH) | 0.040 | % | ISO 62 |
| Shrinkage (200°C, 50.0 µm) 2 | < 2.0 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Breakdown | ASTM D149 | ||
| 23°C, 25.0 µm | 6750 | V | |
| 23°C, 50.0 µm | 9500 | V | |
| 23°C, 125.0 µm | 15000 | V | |
| 23°C, 250.0 µm | 17500 | V |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (23°C, 50.0 µm) | 26.0 | kJ/m² | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 8 to 750 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 23°C, 25 µm | 3000 | MPa | |
| 23°C, 50 µm | 2800 | MPa | |
| 23°C, 130 µm | 2400 | MPa | |
| 23°C, 250 µm | 2200 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| Break, 23°C, 25 µm | 130 | MPa | |
| Break, 23°C, 50 µm | 120 | MPa | |
| Break, 23°C, 130 µm | 110 | MPa | |
| Break, 23°C, 250 µm | 100 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| Break, 23°C, 25 µm | > 150 | % | |
| Break, 23°C, 50 µm | > 150 | % | |
| Break, 23°C, 130 µm | > 150 | % | |
| Break, 23°C, 250 µm | > 150 | % | |
| Trouser Tear Resistance 3(50 µm) | 6.70 | N/mm | ISO 6383-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow 4(0.0500 mm) | 4.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 5(23°C, 0.0500 mm) | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 23°C, 0.0250 mm | 270 | kV/mm | |
| 23°C, 0.0500 mm 6 | 190 | kV/mm | |
| 23°C, 0.125 mm | 120 | kV/mm | |
| 23°C, 0.250 mm | 70 | kV/mm | |
| Dielectric Constant (23°C, 0.0500 mm, 10 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (23°C, 0.0500 mm, 10 MHz) | 2.0E-3 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | 24 hrs |
| 2 . | TM-VX-84 |
| 3 . | 23°C |
| 4 . | below Tg |
| 5 . | 100 V |
| 6 . | 0.25 inch electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 09-523 Solution | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Tenite™ Propionate 360E4861312 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| TAROMID B 280 G5 X0 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Zytel® 70G30L NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Hifax CB 1160 G1 G81493 | LyondellBasell Industries | PP Copolymer | Hifax |