LIHAN® B100EX
| Category: | Nylon 6+PE , Polyamide 6 + PE |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | keL61u_LIHAN-B100EX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low-flexural-strength nylon 6/polyethylene alloy Pamphlet: Low-flexural-strength nylon 6/polyethylene alloy is authorized as patent product of our company. This material has low flexural strength, good flexibility, still maintain basically mechanical properties after six times repeated extrusion process, good processing performance, extrusion process stability, uniform diameter of extruded nylon rod, smooth surface. The material can be used to extruded nylon rod and tube, double-wall corrugated pipe, extruded nylon core material and other extrusion products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.90 to 1.3 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 48.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 100 | % | ISO 527-2 |
| Flexural Modulus | 750 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 to 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® C C110FR | A. Schulman Europe | PC+ABS | RONFALIN® C |
| ExxonMobil™ PP9074MED | ExxonMobil Chemical | PP Random Copolymer | ExxonMobil™ |
| Hyundai EP PA6 LS630 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| LGSTRENE LGH 307 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGSTRENE |
| Softell TKG 259N G21385 | LyondellBasell Industries | PP Copolymer | Softell |