EcoBlend® KCA9341NH
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | EcoBlend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yL4hm1_EcoBlend-KCA9341NH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KCA9341NH is halogen free flame retardant PC/PET resin.KCA9341NH has excellent processing properties and high tenacity.KCA9341NH is mainly used in housing of OA & TV set, panel of stereo equipment,etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 29 | g/10 min | |
| 265°C/2.16 kg | 29 | g/10 min | |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 58.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2350 | MPa | ASTM D790 |
| Flexural Strength | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 79.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-0 5VB | ||
| 2.00 mm | V-0 5VB |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 255 to 265 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 40 to 90 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7500 MF 30 UV LS/1 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| NEOFLON™ EFEP RP-4020 | DAIKIN AMERICA, INC. | Fluoropolymer | NEOFLON™ |
| Chemlon® 100 XHU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Implex® Implex | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Implex® |
| LEXAN™ PC1000 resin | SABIC Innovative Plastics | PC | LEXAN™ |