MARPOL® LL4M 899
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tAEOUX_MARPOL-LL4M-899.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Description: This resin exhibits excellent flow for high speed injection molding applications while providing good tear resistance and ESCR. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.929 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 110 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 16.2 | MPa | |
| Break | 12.4 | MPa | |
| Tensile Elongation (Yield) | 9.3 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant | 524 | MPa | |
| 2% Secant | 483 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 50.0 | °C | ASTM D648 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 86.1 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Polyurethane TC-300 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| FHR EPS 40-5340 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| ENSOFT SL-161-65A | ENPLAST, a Ravago Group Company | TPE | ENSOFT |
| Lushan EJ-1 | Guangzhou Lushan New Materials Co., Ltd | HDPE | Lushan |
| LNP™ THERMOTUF™ MX00619 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOTUF™ |