InnoTuf® HP-1090A
| Category: | TSU-Ester , Polyurethane Thermoset Elastomer, Polyester Based |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yI3WbW_InnoTuf-HP-1090A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-1090A is a high performance 90 shore A polyester polyol based polyurethane formulated for hand-batch or meter mix processing methods. Excellent physical properties can be obtained with a post cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.13 | g/cm³ | |
| Cured | 1.16 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 1.0 to 1.5 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 15.0 | mg | ASTM D4060 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (Split) | 20 | kN/m | ASTM D470 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 82 Mix Ratio by Volume: 77 | ||
| Demold Time (66°C) | 60 to 180 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 43°C 1 | 0.60 | Pa·s | |
| 43°C 2 | 0.85 | Pa·s | |
| 43°C 3 | 1.5 | Pa·s | |
| Curing Time 4 | 1.8E+2 | hr | |
| Gel Time | 10 to 16 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 85 to 95 | ASTM D2240 | |
| Tensile Strength | 31.0 | MPa | ASTM D638 |
| Tensile Elongation at Break | 470 | % | ASTM D638 |
| Tear Strength | 66.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 16 hours at 150°F + 7 days at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PBT EN225 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| Moplen EP649N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| DOMAMID® 66G15 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Flontech® FT-STST50-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| GELOY™ XTPMFR10 resin | SABIC Innovative Plastics Asia Pacific | ASA+PC | GELOY™ |