Generic PPS, Linear - Glass Fiber
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xfRcbR_Generic-PPS-Linear---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPS, Linear - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.40 - 1.92 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.16 - 0.62 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.048 - 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5000 - 18100 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 67.9 - 163 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 0.79 - 1.7 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4000 - 15200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 98.5 - 226 | MPa | ISO 178 |
| Coefficient of Friction | 0.15 - 0.50 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 8.9 - 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 249 - 265 | °C | ISO 75-2/A |
| Continuous Use Temperature | 220 | °C | ASTM D794 |
| CLTE - Flow | 2.3E-5 - 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.40 - 5.2 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 - 2.5E+12 | ohms | IEC 60093 |
| Insulation Resistance (23°C) | 1.0E+4 - 2.5E+12 | ohms | IEC 60167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 135 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Middle Temperature | 320 - 327 | °C | |
| Front Temperature | 330 - 338 | °C | |
| Processing (Melt) Temp | 318 - 330 | °C | |
| Mold Temperature | 152 - 165 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPS, Linear - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VYPET VNT 840 | Lavergne Group | PET | VYPET |
| Generic Acetal (POM) Copolymer - PTFE Fiber | Generic | Acetal (POM) Copolymer | Generic |
| KRATON® D1161 J | Kraton Polymers LLC | SIS | KRATON® |
| Karina BEIGE PVC COMPOUND -E 700-08/166-B | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KEBAFLEX® E 50.1 | BARLOG plastics GmbH | TPV | KEBAFLEX® |