EXPLORE® CT PP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Matrix Polymers |
| Trademark: | EXPLORE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0QWhv0_EXPLORE-CT-PP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Explore CT PP is a rotomoulding composite technology based on a dual layer system designed to provide ultimate performance. The technology is based on a polypropylene (PP) outer layer (XP9041) and a polyolefin modified (XP9042) inner layer. The system combines the beneficial properties of the PP with improved impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact (23°C, 6.00 mm) | 95.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 120 | °C | ISO 306/A50 |
| Melting Temperature | 160 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9B21730 H | 4Plas | Nylon 6 | 4MID® |
| Latilub 82-05GR G/30 | LATI S.p.A. | Nylon 12 | Latilub |
| LEXAN™ 223R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| MAJORIS G551/20 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| LUVOCOM® 6-8826 | Lehmann & Voss & Co. | Nylon 12 | LUVOCOM® |