Hanwha Total PP BI830
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xGePmy_Hanwha-Total-PP-BI830.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BI830 is a highly isotactic block copolymer with high flowability, high strength, and high crystallinity compared to general PP, and is an RTPO (Reactor made Thermoplastic Polymer Olefin) with a high content of ethylene-propylene rubber. It shows an excellent balance of impact resistance (room temperature Izod NB) and strength due to high crystalline technology and the most appropriate rubber design. BI830 has high flowability due to its high melt index, making the product useful in automobile bumpers and the corresponding compound material for large scale parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 40 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 18.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 75 | % | ASTM D638 |
| Flexural Modulus | 834 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 98 | J/m | ASTM D256 |
| 23°C | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 98.0 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 60 | ASTM D2457 |
| Additional Information |
|---|
| Dupont Impact Strength, SAMSUNG TOTAL, -20°C: 500 kg/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 - 200 | °C | |
| Middle Temperature | 200 - 240 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Pressure | 98.1 - 245 | MPa | |
| Holding Pressure | 78.5 - 226 | MPa |
| Injection instructions |
|---|
| Cooling Time: 25 to 40 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-GP4-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| TECHLEN M7472(U) | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| WELLAMID Nylon 6000 MF 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Ferro PP LPP25BK51BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hoffman PVC V7-54 | Hoffman Plastic Compounds Inc. | PVC, Rigid | Hoffman PVC |