RALUPOL® UP 2200
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | RALUPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | x5WTdz_RALUPOL-UP-2200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Organically filled Polyester moulding compound Low post-shrinkage, good electrical and mechanical properties, high surface quality and good colour stability (non-yellowing) Primary application(s): Oven fittings This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 to 1.90 | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 to 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow 1 | 0.70 to 1.0 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 2.0 | % | ISO 62 |
| Post Shrinkage 2 | 0.10 to 0.40 | % | ISO 2577 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature | IEC 60216 | ||
| <50 h | 190 | °C | |
| 20,000 h | 130 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 165 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 5000 to 8000 | MPa | ISO 527-2 |
| Tensile Stress (Injection Molded) | 50.0 to 70.0 | MPa | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 8000 to 10000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 90.0 to 120 | MPa | ISO 178 |
| Compressive Stress | 150 to 200 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.0 to 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (Injection Molded) | 7.0 to 12 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 110 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 70.0 to 120 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 100°C) | 1.5E-5 to 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.50 to 0.60 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 to 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by RASCHIG) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 70.0 | °C | |
| Front Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 100 to 115 | °C | |
| Mold Temperature | 165 to 180 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa | |
| Screw Speed | 70 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 47 NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Karina FUM\u00C9 MBATCH (SP31452) -E 27/ 8-GIN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KEBAPEAK® PEEK XS1700 | BARLOG plastics GmbH | PEEK | KEBAPEAK® |
| POLIMAXX 320PC | IRPC Public Company Limited | SAN | POLIMAXX |
| Akulon® Ultraflow K-FHG6/B | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |