Maxxam™ FR PP301 SHI BK268
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ FR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wvvmaV_Maxxam-FR-PP301-SHI-BK268.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene compound, flame retardant |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.2 - 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 23.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 1250 | MPa | ASTM D790 |
| Flexural Strength 3 | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 130 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed, 3.20 mm) | 100 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ABS 1001 TR-AC | ROMIRA GmbH | ABS | Rotec® ABS |
| Chemical Resources LLD100929 | Chemical Resources, Inc. | LLDPE | Chemical Resources |
| Elastollan® 1154 D | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| EPOPLEN PP CFR 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | PP, Unspecified | EPOPLEN |
| Plaslube® TPX-PA6-95002 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |