Hanwha Total PP GH42W
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | waETeD_Hanwha-Total-PP-GH42W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GH42W is a fire-resistant G/F modified polypropylene compound modified by filling glass fiber to improve mechanical rigidity and heat-resistance. It also possesses excellent flame retardancy. This product can be produced modifying a variety of base PPs, including HIPP (High Isotactic Polypropylene), in HANWHA TOTAL's special processing technology. G/F modified PP is commonly used in making products such as car switch covers, electric tool housings and the like requiring high rigidity, high heat resistance and flame retardancy. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 0.30 - 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 88.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Apparent Bending Modulus | 108 | MPa | ASTM D747 |
| Flexural Modulus | 4120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 162 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 220 | °C | |
| Middle Temperature | 180 - 220 | °C | |
| Front Temperature | 180 - 220 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 58.8 - 108 | MPa | |
| Back Pressure | 0.490 - 0.981 | MPa | |
| Screw Speed | 20 - 70 | rpm |
| Injection instructions |
|---|
| Injection Speed: max |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-Comp™ PPBGF30-E | Southland Polymers | PP Impact Copolymer | Pro-Comp™ |
| Shin-Etsu Elastomer KEG-2000-30A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| BCC Resins MB 1000 | BCC Products Inc. | TS, Unspecified | BCC Resins |
| DENKA ABS SE-10 | Denka Company Limited | ABS | DENKA ABS |
| LOXIM 315 01 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |