LNP™ STAT-KON™ ME006 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZPw6CH_LNP-STAT-KON-ME006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* ME006 is a compound based on Polypropylene resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound MC-1006 Product reorder name: ME006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17300 | MPa | ASTM D638 |
| -- | 14000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 58.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/5 |
| Break 3 | 57.0 | MPa | ASTM D638 |
| Break | 55.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 0.50 | % | ASTM D638 |
| Yield | 0.50 | % | ISO 527-2/5 |
| Break 5 | 0.50 | % | ASTM D638 |
| Break | 0.50 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 12300 | MPa | ASTM D790 |
| -- 7 | 12300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 58.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 42 | J/m | ASTM D256 |
| 23°C 9 | 4.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 83 | J/m | ASTM D4812 |
| 23°C 10 | 4.8 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.7 | J | ASTM D3763 |
| -- | 3.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 153 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 153 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 132 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 125 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 UV | RTP Company | Nylon 66 | RTP |
| RTP 305 TFE 15 FR | RTP Company | PC | RTP |
| Starflam A28UL | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| MARPOL® LL4M 885 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Sylvin 4240-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |