| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wLaF9G_Ryton-R-4-232NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® R-4-232NA 40% glass fiber reinforced polyphenylene sulfide compound complies with United States Food and Drug Administration (FDA) and European Union (EU 10/2011 and 1183/2012) regulations for use as a component of articles intended for repeat use in contact with all types of foods. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.20 | % | |
| Across Flow : 3.20 mm | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 104 | ||
| R-Scale | 122 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 179 | MPa | ASTM D638 |
| -- | 170 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.2 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 14000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 228 | MPa | ASTM D790 |
| -- | 245 | MPa | ISO 178 |
| Compressive Strength | 275 | MPa | ASTM D695 |
| Poisson's Ratio | 0.43 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 91 | J/m | ASTM D256 |
| -- | 9.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact | |||
| 3.18 mm | 450 | J/m | ASTM D4812 |
| -- | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -50 to 50°C | 1.5E-5 | cm/cm/°C | |
| Flow : 100 to 200°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -50 to 50°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 100 to 200°C | 8.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.31 | W/m/K | |
| UL Temperature Rating | 200 to 220 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 3.90 | ||
| 25°C, 1 MHz | 3.90 | ||
| Dissipation Factor | ASTM D150 | ||
| 25°C, 1 kHz | 2.0E-3 | ||
| 25°C, 1 MHz | 2.0E-3 | ||
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 150 | V | UL 746 |
| Insulation Resistance 1(90°C) | 1.0E+12 | ohms |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 5VA | UL 94 | |
| Oxygen Index | 50 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 95%RH, 48 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT SV1081 | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Network Polymers PP PPB 25 0802 GF10 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| ALCOM® PA66 910/1.1 CF10 PTFE10 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Axiall PVC 5006 White | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Formolene® L62009H | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |