Wanthane® WHT-1565IC
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | Wanthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vG0uP8_WanthaneWHT1565IC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYPE: Polyester-based grade Extrusion and injection molding grade FEATURES: Free of platicizer, excellent abrasion and slip resistance, low temperature flexibility, good processability Applications: Electronic Parts, rigid / flexible composite systems, tools, shoes, profiles, etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| DIN Abrasion | 50.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 3.00 | MPa | ASTM D412 |
| 300% strain | 6.00 | MPa | ASTM D412 |
| Tensile Strength (Break) | 25.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 750 | % | ASTM D412 |
| Tear Strength | 70.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 24 hr | 22 | % | ASTM D395 |
| 70°C, 22 hr | 55 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D3418 |
| Vicat Softening Temperature | 63.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 175 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 185 | °C | |
| Mold Temperature | 23 | °C | |
| Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 100 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 165 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 175 | °C | |
| Cylinder Zone 4 Temp. | 180 | °C | |
| Adapter Temperature | 185 | °C | |
| Die Temperature | 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 925 | Salflex Polymers Ltd. | HDPE | Salflex |
| ExxonMobil™ PP7033N | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Karina IVORY PVC COMPOUND -E 90850-35/1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PP KM-Y093R | KMI Group, Inc. | PP Random Copolymer | KMI PP |
| Kepamid® 2320CF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |