P84® NT1
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | P84® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v5ST9R_P84-NT1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advantages of Polyimide P84®NT To overcome the above-mentioned limitations, Evonik Fibres GmbH is now offering Polyimide P84®NT in powder or granulate form, which is processable by employing common sinter technologies such as hot compression moulding or direct forming. The high mechanical stability and the impact resistance of P84®NT parts ensure good machinability with standard tools. Parts made of Polyimide P84®NT are excellent performers in thermally and mechanically stressed applications. This novel material features a high glass transition temperature of 337-364°C and a rigid structure (3705 MPa flexural modulus, 188 MPa strength in a three-point-bending experiment), combined with a high elongation at break of over 11 percent. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3580 | MPa | ISO 527-2 |
| Tensile Stress | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Compressive Modulus | 1960 | MPa | ISO 604 |
| Compressive Stress | 470 | MPa | ISO 604 |
| Compressive Strain at Break | 58 | % | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 343 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 319 | °C | ISO 75-2/Af |
| Glass Transition Temperature | 337 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength 1 | 22 | kV/mm | IEC 60243-1 |
| Note Message | |
|---|---|
| 1 . | AC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A50B01 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| Shin-Etsu Elastomer FE-341U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| ULTEM™ 9090 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Ultramid® A3L HP BK20465 | BASF Corporation | Nylon 66 | Ultramid® |
| Niplene F15 | Soredi S.p.a. | PP Homopolymer | Niplene |