Spartech Polycom SC7-7010UR
| Category: | PC , Polycarbonate |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ukFgfp_Spartech-Polycom-SC7-7010UR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC7-7010UR is a medium viscosity PC resin for injection molding that features a mold release package and UV stabilizer. It is heat stabilized and lubricated for good processing characteristics. Polycarbonate resins span a wide range of physical properties that combine to make it one of the toughest, most versatile of all engineering thermoplastics. It is well known for its exceptional impact resistance, plus it has outstanding mechanical, electrical, and optical properties. A very versatile product for a wide variety of applications, Spartech SC7-7010UR is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 120 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 94.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 770 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 137 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 271 - 282 | °C | |
| Front Temperature | 282 - 299 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-709H | CHI MEI CORPORATION | ABS | POLYLAC® |
| SCHULAMID® 66 GF 15 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Styrolution PS 168N/L | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| ESTADIENE 0835 GF | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Petrotene® PP A3 G20 PRTA010 PH301 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |