Hostalen ACP 5831 D
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U0wnP6_Hostalen-ACP-5831-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostalen ACP 5831 D is a high density polyethylene (HDPE) resin used in small blow molding applications such as thin-wall packaging, consumer goods and toys. It exhibits a very good combination of high stiffness and high stress cracking resistance. Hostalen ACP 5831 D is delivered in pellet form, demonstrates good organoleptic properties, contains antioxidants and has a broad molecular weight distribution. Hostalen ACP 5831 D is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ISO 1183 |
| Apparent Density | > 0.50 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | |
| 190°C/21.6 kg | 22 | g/10 min | |
| 190°C/5.0 kg | 1.2 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Nonionic Surfactant) | 150 | hr | ASTM D1693B |
| FNCT 1(80°C) | 8.0 | hr | ISO 16770 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 60.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1350 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (-30°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Tensile Impact Strength (-30°C) | 75.0 | kJ/m² | ISO 8256/1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | 3.5 MPa, 2% Igepal BC/9 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V145-70E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Daelim Po1y® LL-32HF | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Hostacom G4 R01 Black | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LIHAN® A703 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| SCHULAMID® 6 GF 30 FR 2 BLACK HL3 | A. Schulman Europe | Nylon 6 | SCHULAMID® |