TECHNYL® C 216 V30 BLACK Z/4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ugArKW_TECHNYL-C-216-V30-BLACK-Z-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 216 V30 Black Z/4 is a polyamide 6, reinforced with 30% of glass fibre, for injection moulding. This product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.35 | -- | % | |
| Flow | 0.65 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9600 | 6200 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 190 | 110 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.8 | 4.5 | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 8000 | -- | MPa | ASTM D790 |
| -- | 9500 | 5500 | MPa | ISO 178 |
| Flexural Strength | 235 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 32 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 120 | -- | J/m | ASTM D256 |
| 23°C | 14 | 24 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | -- | °C | ASTM D648, ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 190 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 3.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.80 | 4.50 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 475 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 245 to 250 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| Tekudur MW/GF 20 | TEKUMA Kunststoff GmbH | PBT | Tekudur |
| HiFill FR® PA6/6,6 FR NAT | Techmer Engineered Solutions | Nylon 66/6 | HiFill FR® |
| Petrothene® LM600500 | LyondellBasell Industries | HDPE | Petrothene® |
| OTECH TPE OTE7030 - Cable Jacket | OTECH Corporation | TPE | OTECH TPE |