Ultramid® B3GM35 Q611
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uBDMnQ_Ultramid-B3GM35-Q611.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3GM35 Q611 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade. Applications Typical applications include industrial articles requiring medium rigidity and high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.48 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.7 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8000 | 5000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 120 | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 12 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 8.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 50 | -- | kJ/m² | |
| 23°C | 50 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| CLTE - Flow | 3.8E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.020 | 0.020 | ||
| 1 MHz | 0.020 | 0.020 | ||
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP3004FRF | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| AVP™ GYY01CP | SABIC Innovative Plastics | Nylon 66 | AVP™ |
| Karina GRAY PVC COMPOUND 828-18/447-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostalen 4731 B | LyondellBasell Industries | HDPE | Hostalen |
| Innothane® FM-2080 | Innovative Polymers, Inc. | TSU | Innothane® |