SAMAT 5003N5
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | POLYROCKS CHEMICAL CO., LTD |
| Trademark: | SAMAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | trG1LR_SAMAT-5003N5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAMAT™ 5003N (+) are halogen-free environmental polypropylene (PP) with phosphorus and nitrogen as the flame retardant elements. The synergistic effect of coagulation phase and gas phase on flame retardation enhances the flame retardant efficiency, and the catalytic mechanism accelerates the melting and dropping of the system. The flammability can reach UL94-V2 (0.75mm,1.5mm and 3.0mm) and pass the water immersion test at 70°C for 168hrs (UL746C) and GWIT 750°C and GWFI 960°. They have the characteristics of low density of finished products, low smoke and little corrosion to molds. 5003N (+) pass UL tests and meet the requirements of RoHS, SVHC, PFOS&PFOA, 16P, Halogen-free and PAHs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | % | ASTM D638 |
| Flexural Modulus | 1700 | MPa | ASTM D790 |
| Flexural Strength | 38.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 70 | J/m | ASTM D256 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1 | UL 746C, UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Flammability after water-boiling testing at 70°C for 168 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSH 6093 | Marco Polo International, Inc. | PS (HIPS) | MARPOL® PSH |
| Matrixx 34S5201 | The Matrixx Group, Inc. | PBT | Matrixx |
| Yuyao PPO SE1GFN3-780 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| ADMER™ NF837E | Mitsui Chemicals Europe GmbH | LLDPE | ADMER™ |
| HiFill FR® PA6/6 GF40 FR HS L | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |