Vydyne® R543
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tiH3DZ_Vydyne-R543.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R543 is general purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow and mold release. Glass-reinforced Vydyne resins provide a higher heat distortion temperature, better resistance to creep, higher impact and better dimensional stability when compared with unreinforced PA66. This product has good chemical resistance to a broad range of chemicals, including many aliphatic and aromatic hydrocarbons found in most solvents, gasoline, hydraulic fluids, greases and machine oils. Vydyne R543 resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts. Typical Applications/End Uses: To come |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.60 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 14800 | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 225 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12500 | 9400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 340 | 250 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 13 | 14 | kJ/m² | |
| 23°C | 14 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 87 | 90 | kJ/m² | |
| 23°C | 92 | 95 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 13 | 13 | kJ/m² | |
| 23°C | 13 | 19 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 1.6E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 125 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 110 | -- | °C | |
| 1.50 mm | 110 | -- | °C | |
| 3.00 mm | 110 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.750 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 22 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 5 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 4 | -- | ||
| 3.00 mm | PLC 4 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Oxygen Index | 25 | -- | % | ISO 4589-2 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials - (thickness d = 1mm) | + | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4000 A-1230 L | RTP Company | PPA | RTP |
| Thermylene® P6-20FG-0153 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Bayblend® FR3100 TV | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| KPOL-HDPE HD K-0.35/955 BO | KPOL Chem Co. | HDPE | KPOL-HDPE |
| Braskem PP 5D49 | Braskem America Inc. | PP Homopolymer | Braskem PP |