BorPure™ RE216CF
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | BorPure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nKL51G_BorPure-RE216CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BorPure RE216CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. BorPure RE216CF contains antiblock but no slip agent. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C, Injection Molded) | 800 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Static) | 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD | 450 | MPa | ISO 527-3 |
| TD | 450 | MPa | ISO 527-3 |
| Tensile Strength | ISO 527-3 | ||
| MD | 35.0 | MPa | ISO 527-3 |
| TD | 30.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture | 600 | % | ISO 527-3 |
| TD : Fracture | 600 | % | ISO 527-3 |
| Instrumented Puncture Test - Total Penetration Energy | 200 | J/cm | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 145 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | > 120 | ASTM D2457 | |
| Haze | < 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Specific film values evaluated on chill roll films, produced with Borealis internal standard conditions with a thickness of 50 µm.When compared to films which were produced under other conditions. It should be taken into account that the film properties are strongly dependent on the processing conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 203 | RTP Company | Nylon 66 | RTP |
| Quantum Composites QC-8800 FR2X | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| BUPLEN® 6131 | LUKOIL Bulgaria Ltd. | PP Homopolymer | BUPLEN® |
| InnoTuf® HP-2120A | Innovative Polymers, Inc. | TSU-Ether | InnoTuf® |
| OTECH ALLOY OTO8150LSZH - Riser Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |