APTIV® 1103
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | APTIV® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tcyGbM_APTIV-1103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
APTIV® 1100 series films are the mineral filled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications. APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom. APTIV 1100 has a unique combination of properties providing high temperature performance, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users. APTIV 1100 series provides a higher modulus and lower coefficient of linear thermal expansion over the APTIV 1000 series. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.54 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 0.0500 mm, 50% RH) | 0.090 | % | ISO 62 |
| Shrinkage 2 | |||
| MD : 200°C, 50.0 µm | < 0.50 | % | |
| TD : 200°C, 50.0 µm | < 0.50 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (23°C, 50.0 µm) | 4.00 | kJ/m² | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 25 to 125 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| MD : 23°C, 25 µm | 5500 | MPa | |
| TD : 23°C, 25 µm | 4500 | MPa | |
| MD : 23°C, 50 µm | 5500 | MPa | |
| TD : 23°C, 50 µm | 4500 | MPa | |
| MD : 23°C, 100 µm | 5000 | MPa | |
| TD : 23°C, 100 µm | 4500 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 23°C, 25 µm | 70.0 | MPa | |
| TD : Break, 23°C, 25 µm | 70.0 | MPa | |
| MD : Break, 23°C, 50 µm | 90.0 | MPa | |
| TD : Break, 23°C, 50 µm | 90.0 | MPa | |
| MD : Break, 23°C, 100 µm | 90.0 | MPa | |
| TD : Break, 23°C, 100 µm | 90.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23°C, 25 µm | > 10 | % | |
| TD : Break, 23°C, 25 µm | < 10 | % | |
| MD : Break, 23°C, 50 µm | > 10 | % | |
| TD : Break, 23°C, 50 µm | < 10 | % | |
| MD : Break, 23°C, 100 µm | > 5.0 | % | |
| TD : Break, 23°C, 100 µm | < 10 | % | |
| Trouser Tear Resistance 3 | ISO 6383-1 | ||
| MD : 50 µm | 5.00 | N/mm | |
| TD : 50 µm | 6.00 | N/mm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow 4(0.0500 mm) | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | ASTM E1461 | ||
| -- 5 | 0.61 | W/m/K | |
| -- 6 | 1.3 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 7(23°C, 0.0500 mm) | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 0.0500 mm) | 200 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 0.0500 mm, 10 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (23°C, 0.0500 mm, 10 MHz) | 1.0E-3 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | 24 hrs, 23°C |
| 2 . | TM-VX-84 |
| 3 . | 23°C |
| 4 . | below Tg |
| 5 . | Through Plane |
| 6 . | In-Plane |
| 7 . | 100 V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (PMMA) M/21 | A. Schulman Europe | Acrylic (PMMA) | POLYMAN® |
| EL-Lene™ H5480S | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| POLIMAXX 3375RM | IRPC Public Company Limited | PP Random Copolymer | POLIMAXX |
| TECHNYL® A 216 V20 BLACK 21N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Sylvin 8773-60D White 1406 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |