Genestar™ GN2450
| Category: | Nylon 9T , Polyamide 9T |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | Genestar™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zd15Oq_Genestar-GN2450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GN2450 features high strength and modulus. It is well suited for FPC sliders and IC sockets, as well as other components that require modulus and dimensional precision. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (320°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 1.00 mm | 0.10 | % | |
| Across Flow : 1.00 mm | 0.50 | % | |
| Water Absorption 1(Equilibrium, 40°C, 95%RH) | 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 200 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.1 | % | ASTM D638 |
| Flexural Modulus | 14000 | MPa | ASTM D790 |
| Flexural Strength | 270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 285 | °C | ASTM D648 |
| Glass Transition Temperature | 125 | °C | |
| Melting Temperature | 306 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (10.0 GHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (10.0 GHz) | 0.010 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 2(320°C, 500.0 µm) | 3.70 | cm | |
| Weld Elongation | 0.40 | % | ASTM D638 |
| Weld Strength | 40.0 | MPa | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | 750kgf |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Impact Copolymer CP400 | M. Holland Company | PP Impact Copolymer | MTEGRITY™ PP Impact Copolymer |
| NOVALAC FM 4056P | Vyncolit N.V. | Phenolic | NOVALAC |
| Dugdale PVC Rigid Extrusion - Water White Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| Hifax TYC 852X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Plaslube® PA6/6 CF33 ML2 BK | Techmer Engineered Solutions | Nylon 66 | Plaslube® |