Hifax TKC 115X Black
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | somVES_Hifax-TKC-115X-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hifax" TKC 115X is a 30% mineral filled, impact modified polypropylene copolymer for injection molding. It combines excellent stiffness/impact balance, excellent dimensional staiblity, and very low shrinkage with good flowability properties. The grade has been specifically designed for molding of automotive painted exterior trim parts. The grade is available in black, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Shrinkage | ISO 2554 | ||
| 23°C 1 | 0.50 | % | |
| 23°C 2 | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 16.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 25 | % | ISO 527-2/50 |
| Flexural Modulus 3(23°C) | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 3.5 | kJ/m² | |
| 23°C | No Break |
| Note Message | |
|---|---|
| 1 . | 48 hr, 40 bar, q. |
| 2 . | 48 hr, 40 bar, l. |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P240 LHSV | Nilit Plastics | Nylon 66 | POLYNIL® |
| 4DUR® 9K22720 | 4Plas | PBT | 4DUR® |
| OP - PPO PPOX-210 | Oxford Polymers | PPE+PS | OP - PPO |
| Monprene® SP-14966 | Teknor Apex Company | TPE | Monprene® |
| LNP™ THERMOCOMP™ QF00A compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |