CERTENE™ LLI-10030
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xHqesf_CERTENE-LLI-10030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLI-10030 is a certified prime resin specially designed for injection molding applications requiring good low temperature resistance. LLI-10030 features superior processability , excellent low temperature toughness, gloss, and ESCR. LLI-10030 conforms with FDA regulation 21CFR 177.1520 for food contact articles. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 100 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 7.58 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 75 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 130 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -38.0 | °C | ASTM D746 |
| Additional Information |
|---|
| All test specimens were compression molded according to ASTM D1928 procedure C. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-6830 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| Styropor® P 326 | BASF Corporation | PS (EPS) | Styropor® |
| STYRON™ 665 | Americas Styrenics LLC | PS (GPPS) | STYRON™ |
| Niche PA66GF33BK | Niche Polymer, LLC | Nylon 66 | Niche |
| LG PMMA HI835HS | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |