Starex NH-0825
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sYEgn3_Starex-NH-0825.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex NH-0825 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 41.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2/50 |
| Break | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 18 | % | ISO 527-2/50 |
| Flexural Modulus 2 | |||
| -- | 2200 | MPa | ASTM D790 |
| -- | 2240 | MPa | ISO 178 |
| Flexural Strength 3 | |||
| -- | 65.0 | MPa | ASTM D790 |
| -- | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C) | 23 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 6.35 mm | 220 | J/m | ASTM D256 |
| 23°C 5 | 22 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 83.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 78.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 71.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 89.0 | °C | ISO 306/B50 |
| -- | 91.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 2.50 mm | V-2 | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | Thickness: 4 mm |
| 5 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell PP RQ-18 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| ICORENE® N2004 | ICO Polymers EMEA, A Division of A. Schulman | Plastomer | ICORENE® |
| LEXAN™ 4795R resin | SABIC Innovative Plastics | PPC | LEXAN™ |
| Lucent PP CPP-330 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| LNP™ STAT-LOY™ A3000 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |