Generic SBS
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | X3lKXc_Generic-SBS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic SBS This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.890 - 1.19 | g/cm³ | ASTM D792 |
| 23°C | 0.908 - 0.996 | g/cm³ | ISO 1183 |
| Apparent Density | 0.40 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/5.0 kg | 0.50 - 12 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 0.0 - 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.1 - 3.3 | % | ASTM D955 |
| Transverse flow : 23°C | 1.1 - 2.2 | % | ASTM D955 |
| 23°C | 0.50 - 1.4 | % | ISO 294-4 |
| Solution Viscosity | 22 - 1520 | mPa·s | ASTM D445 |
| Bound Styrene | 28.9 - 40.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 29 - 92 | ASTM D2240 | |
| 23°C | 40 - 92 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 1.63 - 7.45 | MPa | ASTM D638 |
| Yield, 23°C | 4.30 - 27.4 | MPa | ISO 527-2 |
| 23°C | 1.00 - 13.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 380 - 1000 | % | ASTM D638 |
| Fracture, 23°C | 36 - 770 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% strain, 23°C | 0.300 - 3.73 | MPa | ASTM D412 |
| 100% strain, 23°C | 0.700 - 2.45 | MPa | ISO 37 |
| 300% strain, 23°C | 0.600 - 4.49 | MPa | ASTM D412 |
| 300% strain, 23°C | 2.29 - 3.06 | MPa | ISO 37 |
| Tensile Strength | |||
| Yield, 23°C | 1.30 - 33.1 | MPa | ASTM D412 |
| Yield, 23°C | 2.20 - 33.0 | MPa | ISO 37 |
| Fracture, 23°C | 2.00 - 7.40 | MPa | ASTM D412 |
| Fracture, 23°C | 5.00 - 33.0 | MPa | ISO 37 |
| 23°C | 3.70 - 20.1 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Fracture, 23°C | 350 - 1200 | % | ASTM D412 |
| Fracture, 23°C | 430 - 910 | % | ISO 37 |
| Tear Strength | |||
| 23°C | 9.00 - 78.6 | kN/m | ASTM D624 |
| 23°C | 15 - 32 | kN/m | ISO 34-1 |
| Compression Set | |||
| -- | 10 - 36 | % | ASTM D395 |
| 23°C | 14 - 35 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 144 - 170 | °C | |
| Middle Temperature | 152 - 170 | °C | |
| Front Temperature | 158 - 171 | °C | |
| Nozzle Temperature | 170 - 196 | °C | |
| Processing (Melt) Temp | 189 - 221 | °C | |
| Mold Temperature | 22.5 - 37.8 | °C | |
| Injection Pressure | 4.14 - 6.19 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SBSThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 145 - 150 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 150 - 160 | °C | |
| Cylinder Zone 4 Temp. | 160 - 170 | °C | |
| Cylinder Zone 5 Temp. | 165 - 170 | °C | |
| Die Temperature | 175 - 180 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SBSThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bamtac BTR620A | Ningbo Bamtac New Material Col, Ltd. | SBS | Bamtac |
| Arak LLDPE BD2450AA | Shazand (Arak) Petrochemical Corporation | LLDPE | Arak LLDPE |
| Escorene™ Ultra LD 728.61 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| LNP™ COLORCOMP™ J1000AE compound | SABIC Innovative Plastics | PESU | LNP™ COLORCOMP™ |
| TORZEN® HV125A NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |