Jackdaw PLA HW10NT6622
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Jackdaw PLA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qrO98Y_Jackdaw-PLA-HW10NT6622.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jackdaw PLA HW10NT6622 is a Polylactic Acid (PLA) product. It can be processed by extrusion and is available in Europe. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 190 | % | ASTM D638, ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 50.0 | °C | ASTM D648 |
| Melting Temperature | 148 | °C | ISO 1218, ASTM D2117 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® P 70 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Unipren® Elastomers A3 NTLA010 65A UP323 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| NEFTEKHIM PE 4121N (22401) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| DuPure® SR 79 | Ducor Petrochemicals BV | PP Impact Copolymer | DuPure® |
| Huaxia Shenzhou PFA DS708-B | Shandong Huaxia Shenzhou New Material Co., Ltd. | PFA | Huaxia Shenzhou |