Kangxi® PP-30GF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Wuxi Kangxi Plastics Technology Co.,Ltd. |
| Trademark: | Kangxi® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qncD0d_KangxiPP30GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kangxi®PP-30GF is a polypropylene product, and the filler is 30% glass fiber reinforced material. It can be processed by injection molding and is available in the Asia-Pacific region. Kangxi®PP-30GF applications include electrical appliances and the automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 75.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 4 | 5000 | MPa | ASTM D790 |
| Flexural Strength 5 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 160 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 150 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weather Resistance - 24 hr (23°C) | 0.020 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 180 - 230 | °C | |
| Middle Temperature | 180 - 230 | °C | |
| Front Temperature | 180 - 230 | °C | |
| Processing (Melt) Temp | 220 - 245 | °C | |
| Mold Temperature | 30 - 60 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 10 mm/min |
| 3 . | 10 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP1B40 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| TOLEN H033 FF | SIBUR, LLC | PP Homopolymer | TOLEN |
| UBESTA 3024NUX | UBE Industries, Ltd. | Nylon 12 | UBESTA |
| Diakon® CLG903 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Sylvin 9915-92FUV Brown 7404 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |