RTP 4000.3
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r7gMB1_RTP-4000-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 1.4 | % | ASTM D955 |
| Moisture Content | 0.050 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.5 - 2.5 | % | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 210 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 302 - 329 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| apilon 52® A-52/1 | API SpA | TPU-Polyester | apilon 52® |
| HANWHA 7600 | Hanwha Chemical | HDPE | HANWHA |
| HiFill® HIPS GF30 | Techmer Engineered Solutions | PS (HIPS) | HiFill® |
| LUVOCOM® 80-8584 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| ISPLEN® PR210 G4E | REPSOL | PP Random Copolymer | ISPLEN® |