3M™ Dyneon™ PTFE Compound TF 3215
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE Compound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qbd3z0_3M-Dyneon-PTFE-Compound-TF-3215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.07 | g/cm³ | ASTM D4745-06 |
| Apparent Density | 0.45 | g/cm³ | ASTM D4894-07 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D4894-07 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore D) | 72 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Break) | 20.0 | MPa | ASTM D4745-06 |
| Tensile Elongation 3(Break) | 250 | % | ASTM D4745-06 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 70.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | Measured on sintered moldings |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 5100 GY | POLY GIN | PC | MARCOBLEND |
| SCHULAMID® 66 MV HI TST | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Shin-Etsu RTV KE-40RTV | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Starex TF-0956 | SAMSUNG SDI CO., LTD. | Acrylic (PMMA) | Starex |
| Sylvin 86017-50 Red 6238 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |