Cevian®-V T140
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ShKVRS_Cevian--V-T140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V T140 is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America. The main characteristics are: high strength. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 48.3 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 110 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 88.9 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 88.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Specific Gravity, ASTM D792, 73°F, 50% RH: 1.07Water Absorption, ASTM D570, 73°F, 24 hr: 0.3 % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 220 - 240 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 48.9 - 60.0 | °C | |
| Injection Pressure | 34.5 - 103 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.689 - 2.07 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safrene® M 5010PE 100 | Safripol (PTY) LTD | HDPE | Safrene® |
| HANWHA EVA 1326 | Hanwha Chemical | EVA | HANWHA EVA |
| Hifax TRS 372P | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 6920X08 Green 3219 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Polygen SFG6C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |