POCAN® S 7020 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qKbBSG_POCANS7020000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, non-reinforced, injection molding,Extrusion, flame retardant, improved impact strength |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.38 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (270°C/5.0 kg) | 50.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 250°C, 2.00mm 1 | 1.8 | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.40 | % | ISO 294-4 |
| Flow direction : 250°C, 2.00mm 3 | 1.8 | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 15 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2300 | MPa | ISO 899-1 |
| 1000 hr | 1600 | MPa | ISO 899-1 |
| Flexural Modulus 5(23°C) | 2300 | MPa | ISO 178/A |
| Flexural Stress 6 | |||
| 3.5% strain | 70.0 | MPa | ISO 178/A |
| 23°C | 75.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength (23°C) 7 | 5.3 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halving Interval | IEC 60216 | ||
| -- 8 | 5.3 | °C | IEC 60216 |
| -- 9 | 5.8 | °C | IEC 60216 |
| -- 10 | 5.8 | °C | IEC 60216 |
| Temperature index 11 | IEC 60216 | ||
| Electric Strength | 135 | IEC 60216 | |
| Tensile Impact Strength | 120 | IEC 60216 | |
| Tensile Strength | 135 | IEC 60216 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GFHMPR, 11-020; ISO 1043-PBT FR (17) | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 110 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 65 | kJ/m² | ISO 180/1U |
| 23°C | No Break | ISO 180/1U | |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 80.0 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B120 |
| Ball Pressure Test (190°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 12 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.25 | W/m/K | ISO 8302 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.80 | IEC 60250 | |
| 23°C, 1 MHz | 3.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 4.0E-3 | IEC 60250 | |
| 23°C, 1 MHz | 0.024 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index 13 | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; WZ 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; WZ 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | Tensile Impact Strength |
| 9 . | Electric Strength |
| 10 . | Tensile Strength |
| 11 . | 20000 h |
| 12 . | 10°C/min |
| 13 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1905 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| SureSpec HD54-05 | Genesis Polymers | HDPE, HMW | SureSpec |
| Wondel® T TR0 | Nanjing Julong Engineering Plastics Co., LTD | PBT | Wondel® T |
| CENUSIL® M 810 A/B | Wacker Chemie AG | Silicone | CENUSIL® |
| PC-COM™ PC422-50 | Polymer Compounders Limited | PC | PC-COM™ |